Are you looking to buy Polymaker Fiberon PA612-CF15 PolyMide PA612-CF Nylon 1.75 Filament 500g in Australia?
PolyMide PA612-CF will transition to Polymakers Fiberon range and will be sold as Fiberon PA612-CF15 (same product, new name and packaging)
Fiberon is Polymakers new range of composite 3D printing filaments, launching in Q4 2024. Polymaker are transitioning PolyMide PA612-CF and their carbon-fibre / glass fibre reinforced Nylons from the PolyMide family and reintroducing them under the Fiberon product range.
PolyMide™️ PA612-CF is a carbon fibre reinforced nylon filament based on a copolymer of Nylon 6 and Nylon 12. Featuring 15% chopped carbon fibres by weight, this filament has lower moisture sensitivity compared to PA6/66 and PA6-based materials, and better mechanical properties than PA12-based materials. Together with Polymaker's Warp-Free™ and Fiber-Adhesion™ technology, PolyMide™️ PA612-CF offers an optimal balance by combining the advantages of both PA6 and PA12 with optimised fibre reinforcement to deliver a high-performance filament with outstanding potential for industrial engineering, tooling, automotive, and end-use applications.
Tip - Although Nylon 612 is less sensitive to moisture, we highly recommend to use a wear resistant nozzle, to print with the PolyBox™ and to keep it at dry conditions (relative humidity of 15% or less) at all times to maintain the best printing results. Please see "Specifications & FAQ" tab for data, annealing and additional tips.
Features
- Best of PA6 and PA12 - PolyMide™ PA612-CF is a copolymer combining PA6 and PA12 with 15% chopper carbon fibre to deliver high stiffness, tensile strength and heat resistance with lower moisture sensitivity. PolyMide™ PA612-CF offers the best middle ground between PA6 and PA12 and is a great-all-rounder for real-world applications that require the higher mechanical performance and affordability of short-chain nylon (PA6) with the reduced moisture sensitivity of long-chain nylon (PA12).
- Reduced Moisture Sensitivity - In most applications nylon parts absorb moisture from the air. The water molecule increases toughness and durability of the nylon while reducing strength and stiffness. PA6 is more susceptible to absorbing moisture than PA12 and as a result the mechanical properties of PA6 are effected in some application environments. PolyMide™ PA612-CF is less hygroscopic than PA6-CF making it an ideal and cost-effective alternative to PolyMide™ PA6-CF for parts which may be subject to high humidity.
- Excellent Heat Resistance - Featuring a high heat resistance after annealing[1], PolyMide™ PA612-CF offers excellent heat resistance for demanding applications where heat and stress are critical design factors.
- Outstanding Layer Adhesion - Most fibre reinforced materials show a decrease in z-axis layer adhesion when compared with their non-fibre reinforced Nylons, producing a part that is only stronger on the X-Y axis but detrimental to the Z axis. Polymakers Fibre Adhesion™ technology improves the layer adhesion of fibre reinforced materials, by optimising the surface chemistry of the fibres to achieve better dispersion and bonding to the matrix. The implementation of this technology in PolyMide™ PA612-CF not only solves this problem but actually increases Z axis tensile strength creating more isotropic parts that are strong in every direction.
- Warp-Free™ - Warp-Free™ technology enables the production of Nylon-based filaments that can be 3D printed with excellent dimensional stability and near-zero warpage. This is achieved by the fine control of microstructure and crystallisation behaviour of Nylon, which enables the material to fully release the internal stress before solidification. The Warp-Free™ technology in PolyMide™ PA612-CF is designed to work best with minimal bed temperatures.
- Excellent Printability – Unlike many other brands of Nylon filament, PolyMide™ PA612-CF is extremely easy to work with, exhibiting excellent dimensional stability during printing. It is compatible with most filament-based 3D printers capable of reaching 260°C nozzle temperature and no heated bed or chamber is required!
- Uncompromised Quality - Polymakers leading quality control process and rigorous in-house testing ensure reliable printing and consistency across spools and batches.
[1] PolyMide™ PA612-CF displays the best mechanical and thermal properties when fully crystallised. The printed part will not reach full crystallization during the printing process, an additional step is required: Annealing. PolyMide™ PA612-CF can be annealed in the oven at 80˚C for 6 hours right after the printing process.
Technical Data
All PA612-CF specimens were printed with 300°C nozzle temperature, 50°C bed temperature, cooling fan OFF and samples were annealed after printing at 100°C for 16h. Samples were printed with 100% infil, 2 shells and 3 top & bottom layers.
Fiberon PA612-CF15 Thermal Properties
Value | Testing Method | |
Heat Deflection Temperature |
0.45MPa - 175°C HDT Curve |
ISO 75 |
Fiberon PA612-CF15 Mechanical Properties
1. All Dry Status specimens were annealed at 100°C for 16h.
2. All Wet Status specimens were annealed at 100°C for 16h, and immerged in water at 60°C for 48h prior to testing. The
average moisture content of specimens is 2.57%
Dry State Value | Wet State Value | Testing Method | |
Youngs Modulus (X-Y) |
5136.7 ± 192.2 MPa | 3990.8 ± 136.5 MPa | ISO 527, GB/T 1040 |
Youngs Modulus (Z) |
2786.4 ± 78.4 MPa | 2386.8 ± 150.2 MPa | |
Tensile Strength (X-Y) |
91.9 ± 2.0 MPa | 83.1 ± 2.2 MPa | ISO 527, GB/T 1040 |
Tensile Strength (Z) |
48.3 ± 3.9 MPa | 35.6 ± 3.0 MPa | |
Bending Strength (X-Y) |
138.0 ± 2.2 MPa | 118.1 ± 1.6 MPa | ISO 306, GB/T 1633 |
Charpy Impact Strength Notched (X-Y) |
8.1 ± 0.8 kJ/m2 | 7.7 ± 0.5 kJ/m2 | ISO 179, GB/T 9343 |
Data taken from Polymakers Technical Data Sheet and is intended for reference and comparison purposes only. Due to the nature of 3D printing, data should not be used for design specifications or quality control purposes.
Browse more
- Browse Polymaker
- Browse ASA Filament
- Browse ABS Filament
- Browse Nylon Filament
- Browse PC Filament
- Browse PETG Filament
- Browse PLA Filaments (also PLA+)
- Browse PVA Filament
- Browse Silk Filament
- Browse SLA Resin
- Browse Speciality Filament
- Browse TPU Filament