Are you looking to buy Polymaker Fiberon PETG-rCF08 1.75mm Filament 500g in Australia?
Our entry-level composite filament featuring recycled carbon fibers. Inheriting the printability and performance of PETG, while gaining enhanced stiffness from the carbon fiber reinforcement. Print high-speed, moisture-insensitive, and low-creep prototypes with exceptional dimensional accuracy. PETG-rCF08 strikes the perfect balance between affordability and functionality, empowering you to quickly create durable, accurate prototypes.
Features
- Affordable & Easy-to-use - Fiberon™ PETG-rCF08 is a cost-effective recycled carbon fiber reinforced PETG filament billed as the "PLA of engineering materials". It inherits the comprehensive performance of PETG, featuring recycled carbon fiber for enhanced surface texture and improved mechanical properties.
- Recycled Carbon Fibers- Fiberon™ PETG-rCF08 utilizes carbon fibers from end-of-life wind turbine blades, these fibers are certified to the Global Recycled Standard by TÜV Rheinland. The use of recycled carbon fibers delivers a more sustainably sourced composite filament while maintaining the mechanical strength that users come to expect from carbon-fiber reinforcement.
- Dimensional Accuracy & Moisture Insensitivity - By delivering fantastic dimensional accuracy, low moisture sensitivity[1] and low shrinkage during printing, Fiberon PETG-rCF17 is well suited for rapid prototyping and a wide range of functional applications requiring durability, accuracy and surface finish.
-
High Speed Capable - Fiberon PETG-rCF08 has been developed with printer compatibility in mind and is high speed capable, enabling printing up to 300mm/s on suitable high speed printers.
Excellent Surface Finish - Fiberon™ PETG-rCF08 3D prints and renders parts with an attractive surface finish thanks to the PETG's excellent fluidity as a matrix material and the 8% carbon fiber reinforcement.
[1] Low moisture sensitivity does not describe whether the filament should be kept dry for optimal print quality. This description of moisture insensitivity is in the context of the end-use application where extremely moisture sensitive materials like PA6-CF see a significant reduction in mechanical properties as the part absorbs moisture. With PETG-CF moisture absorption is minimal and doesn't impact the mechanical properties of the part. For best printing results PETG-CF should still be kept dry during printing and storage.
All PETG-rCF specimens were printed with 270°C nozzle temperature, 60°C bed temperature, cooling fan 0 - 50%. Samples were printed with 100% infil, 2 shells and 3 top & bottom layers.
Fiberon PETG-CF08 Thermal Properties
Value | Testing Method | |
Glass Transition | 69.7°C | DSC, 10°C/min |
Heat Deflection Temperature |
0.45MPa - 68.6°C HDT Curve |
ISO 75 |
Vicat Softening Temperature | 81.6°C | ISO 306, GB/T 1633 |
Fiberon PETG-CF08 Mechanical Properties
Value | Testing Method | |
Youngs Modulus (X-Y) |
3710.1 ± 151.1 MPa | ISO 527, GB/T 1040 |
---|---|---|
Youngs Modulus (Z) |
2651.9 ± 51.0 MPa | |
Tensile Strength (X-Y) |
59.8 ± 0.3 MPa | ISO 527, GB/T 1040 |
Tensile Strength (Z) |
41.1 ± 4.1 MPa | |
Bending Strength (X-Y) |
94.6 ± 1.3 MPa | ISO 306, GB/T 1633 |
Bending Strength (Z) |
47.8 ± 2.4 MPa | |
Charpy Impact Strength Notched (X-Y) |
4.0 ± 0.9 kJ/m2 | ISO 179, GB/T 9343 |
Data taken from Polymakers Technical Data Sheet and is intended for reference and comparison purposes only. Due to the nature of 3D printing, data should not be used for design specifications or quality control purposes.
Browse more
- Browse Polymaker
- Browse ASA Filament
- Browse ABS Filament
- Browse Nylon Filament
- Browse PC Filament
- Browse PETG Filament
- Browse PLA Filaments (also PLA+)
- Browse PVA Filament
- Browse Silk Filament
- Browse SLA Resin
- Browse Speciality Filament
- Browse TPU Filament