Are you looking to buy Bambu Lab PAHT-CF Filament in Australia?
Looking for Bambu Labs PAHT-CF Filament, Carbon Fiber Nylon Material 1.75mm 1kg in Australia?
Bambu PAHT-CF is a composite of PA12 and carbon fiber. Inheriting the advantages of low water absorption from PA12 and high-performance carbon fiber, Bambu PAHT-CF offers excellent mechanical and thermal properties that can be maintained well even when the prints get wet. Higher Z adhesion layers and flexibility make it ideal for creating engineering parts such as functional prototypes, machining fixtures, injection molds, jigs, and low-volume production parts.
Bambu Labs PAHT-CF Filament
With a 50% lower water absorption rate compared to normal PA-CF,Bambu PAHT-CF maintains excellent mechanical properties and dimensional stability even when exposed to high humidity.
Deflection from Dry to Wet
Mechanical Properties Comparison
| Normal PA-CF | PAHT-CF | |
| Saturated Water Absorption Rate/% ( 25 °C, 55% RH ) | 1.89 | 0.88 |
| Bending Strength - XY/MPa (Dry) | 141 | 140 |
| Bending Strength - XY/MPa (Wet) | 76 | 115 |
| Bending Strength - Z/MPa (Dry) | 47 | 70 |
| Bending Strength - Z/MPa (Wet) | 34 | 58 |
| Bending Modulus - XY/MPa (Dry) | 4480 | 4120 |
| Bending Modulus - XY/MPa (Wet) | 2210 | 3640 |
| Bending Modulus - Z/MPa (Dry) | 1470 | 1700 |
| Bending Modulus - Z/MPa (Wet) | 770 | 1480 |
| Decline rate of mechanical properties after absorbing water/% | 40%-45% | 12%-18% |
- Both PA-CF and PAHT-CF need to be dried at 80°C for 12 hours before printing.
Exceptional Z-bonding
Bambu PAHT-CF shows much higher adhesion in Z layers compared to normal PA-CF,bringing it the ability to withstand high levels of impact or stress without breaking or deforming.
Z-layer Performance
| Normal PA-CF | PAHT-CF | Improved % | |
| Bending Strength - Z/MPa | 47 | 70 | 49% |
| Bending Modulus - Z/MPa | 1470 | 1700 | 16% |
| Impact Strength - Z/(kJ/m²) | 5.7 | 13.3 | 133% |
High Tensile Strength
Bambu PAHT-CF is designed to meet the demands of various industrial and engineering applications where high strength and durability are required.
Designed for high-temperature resistance
The heat deflection temperature of Bambu PAHT-CF is up to 194℃ (0.45MPa)*, making it useful in applications where the printed parts may be exposed to high temperatures without deforming or losing their strength.
*The long-term temperature resistance is related to the structure and usage scenario of the model itself.
Reusable spool
Bambu PAHT-CF comes with a high-temperature resistant spool, which is not prone to deformation in the drying process. Continuing our concept of reducing plastic waste, the spool can also be reused with other Bambu refills.
Accessory Compatibility
| Recommended | Not Recommended | |
| Build Plate | High Temperature Plate Engineering Plate | Cool Plate |
| Hotend | Hotend with Hardened Steel Nozzle (0.6 mm, 0.4 mm, 0.8 mm)* | Hotend with Stainless Steel Nozzle (all size) Hotend with Hardened Steel Nozzle (0.2 mm) |
| Glue | Glue Stick | Liquid Glue |
- As the nozzle size increases, the probability of clogging decreases, but the print quality also decreases. Therefore, it is recommended to use a 0.6 mm Hardened Steel nozzle to avoid clogging while maintaining optimal print quality.
RFID for Intelligent Printing
All printing parameters are embedded in RFID, which can be read through our AMS (Automatic Material System).Load and print! No more tedious setting steps.
Parameters Comparison
| PET-CF | PAHT-CF | |
| Price/kg | $129.99 AUD | $144.99 AUD |
| Composition | PET, carbon fiber | PA 12 and other long-chain PA, carbon fiber |
| Hotend Compatibility | Hardened Steel 0.6 (recommended), 0.4, 0.8 mm | |
| Build Plate Compatibility | Engineering Plate, High Temperature Plate, Textured PEI Plate | |
| Glue | Glue Stick / Liquid Glue | Glue Stick |
| AMS Compatibility | NO | YES |
| Print Speed | < 100 mm/s | < 100 mm/s |
| Toughness (Impact Strength - XY) | 36.0 kJ/m² | 57.5 kJ/m² |
| Strength (Bending Strength - XY) | 149 MPa | 140 MPa |
| Stiffness (Bending Modulus - XY) | 5080 MPa | 4120 MPa |
| Layer Adhesion (Impact Strength - Z) | 4.5 kJ/m² | 13.3 kJ/m² |
| Heat Resistant（HDT, 0.45 MPa） | 205 °C | 194 °C |
| Saturated Water Absorption Rate / % (25 °C，55% RH) | 0.37 | 0.89 |
Recommended Printing Settings
- Drying Settings before Printing - 80 °C, 8 - 12 h
- Pringting and Keeping Container's Humidity - < 20% RH (Sealed, with Desiccant)
- Nozzle Temperature - 260 - 290 °C
- Bed Tempreature (with PVP Glue) - 80 - 100 °C
- Printing Speed - < 100 mm/s
Physicial Properties
- Density - 1.06 g/cm³
- Vicar Softening Temperature - 220 °C
- Heat Deflection Temperature - 194 °C
- Melting Temperature - 225 °C
- Melt Index - 14.4 ± 2.0 g/10 min
Mechanical Properties
- Tensile Strength - 88 ± 7 MPa
- Breaking Elongation Rate - 10.4 ± 0.7 %
- Bending Modulus - 4120 ± 290 MPa
- Bending Strength - 140 ± 8 MPa
- Impact Strength - 57.5 ± 3.4 kJ/m²
Printing Tips
- Bambu PAHT-CF needs proper drying before printing: recommended drying temperature is 80 ℃ for 5 hours in filament dryer, or 90 ℃ for 10 hours on heat bed. (Do not exceed 100 ℃ because the spool may melt). For more details please refer to:  Filament Drying Procedure on WIKI.
- Bambu PAHT-CF has high thermal insulation requirements during the printing process, making it unsuitable for use with open-frame printers.
- For better print results, please refer to: Printing tips for Engineering materials on WIKI.
Browse more
- Browse all Bambu Lab Filament
- Browse all Bambu Lab X1 3D Printer, Spare Parts & Accessories
- Browse all Bambu Lab P1P/P1PS 3D Printer, Spare Parts & Accessories
- Browse all Bambu AMS Spare Parts & Accessories
- Browse all Bambu Lab A1 Mini 3D Printer, Spare Parts & Accessories
- Browse all Bambu Labs
- Browse all Printer Spare Parts
- Browse ASA Filament
- Browse ABS Filament
- Browse Nylon Filament
- Browse PC Filament
- Browse PETG Filament
- Browse PLA Filaments (also PLA+)
- Browse PVA Filament
- Browse Silk Filament
- Browse Speciality Filament
- Browse TPU FilamentÂ
- Check out all our 3D Printing Supplies